Hybrid electrolyte based on PEO and ionic liquid with in situ produced and dispersed silica for sustainable solid-state battery

Abstract

This work introduces the synthesis of hybrid polymer electrolytes based on polyethylene oxide (PEO) and electrolyte solution bis(trifluoromethane)sulfonimide lithium salt/ionic liquid 1-ethyl-3-methyl-imidazolium bis(trifluoromethylsulfonyl)imide (LiTFSI/EMIMTFSI) with in situ produced and dispersed silica particles by the sol–gel method. Conventional preparation of solid polymer electrolytes was followed by desolvation of lithium salt in a polymer matrix of PEO, which, in some cases, additionally contains plasticizers. This one-pot synthesis is an alternative route for fabricating a solid polymer electrolyte for solid-state batteries. The presence of TFSI- reduces the crystallinity of the PEO matrix (plasticizing effect), increases the dissociation and solubility of LiTFSI in the PEO matrix because of a highly delocalized charge distribution, and reveals excellent thermal, chemical, and electrochemical stability. Tetraethylorthosilicate (TEOS) was chosen due to the slow reaction rate, with the addition of (3-glycidyoxypropyl)trimethoxysilane (GLYMO), which contributes to the formation of a silica network. FTIR studies confirmed the interactions between the silica, the polymer salt, and EMIMTFSI. Impedance spectroscopy measurements were performed in a wide range of temperatures from 25 to 70 °C. The electrochemical performance was explored by assembling electrolytes in LiCoO2 (LCO), NMC(811), and LiFePO4 (LFP) coin half-cells. The HPEf15 shows a discharge capacity of 143 mA/g for NMC(811) at 0.1 C, 134 mA/g for LCO, and 139 mA/g for LFP half-cells at 0.1 C and 55 °C. The LFP half-cell with a discharge capacity of 135 mA/g at 0.1 C (safety potential range of 2.8 to 3.8) obtained a cyclability of 97.5% at 55 °C after 100 cycles. Such a type of electrolyte with high safety and good electrochemical performance provides a potential approach for developing a safer lithium-ion battery.